| Page properties | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| ||||||||||
|
10x IP-
SQ
Si is a preferred substrate. Other substrates Substrate must have a refractive index of 1.6 or larger. Glass substrates must have ITO or another film with high refractive index deposited on the printing surface. Si can be used normally.
Observe sample dimensions before loading. For the standard sample holder the sample must be 25 mm × 25 mm and more than 550 μm thick, but not thicker than 700 μm. Contact the tool trainer before loading different samples.
| Application | Parameter | Value |
|---|---|---|
Solid | Hatching (µm) | 1.0 |
| Slicing (µm) | 5.0 | |
| Laser power (%) | 100 | |
| Scan speed (µm/s) | 100000 | |
Shell & scaffold | Hatching (µm) | 0.5 |
| Slicing (µm) | 3.0 | |
| Shell laser power (%) | 100 | |
| Shell scan speed (µm/s) | 100000 | |
| Scaffold laser power (%) | 100 | |
| Scaffold scan speed (μm/s) | 150000 |
25x IP-S
Si is a preferred substrate. Other substrates must have a refractive index of 1.6 or larger. Glass substrates must have ITO or another film with high refractive index deposited on the printing surface.
Observe sample dimensions before loading. For the standard sample holder the sample must be 25 mm × 25 mm and more than 550 μm thick, but not thicker than 0.7 mm700 μm. Contact the tool trainer before loading different samples.
| Application | Parameter | Value |
|---|---|---|
Standard | Hatching (µm) | 0. |
| 4 |
| Slicing (µm) |
| 0. |
| 8 | ||
| Laser power (%) | 50 | |
| Scan speed (µm/s) | 50000 | |
Micro-optics* | Hatching (µm) | 0.1 |
| Slicing (µm) | 0.104 | |
| Laser power (%) | 30 | |
| Scan speed (µm/s) | 100000 |
*Don't use contour lines. Proximity effect will be responsible for producing smooth surfaces.
63x IP-Dip
Glass substrates can be loaded normally, without any extra films. Si can also be used, however the interface finder must be reconfigured to allow for proper operation. Contact the tool trainer if using this setup on Si samples.
Observe sample dimensions before loading. For the standard sample holder the sample must be 25 mm × 25 mm and more than 0.5 mm thick, but not thicker than 0.7 mm. Contact the tool trainer before loading different samples.
| Application | Parameter | Value |
|---|---|---|
Standard | Hatching (µm) | 0.2 |
| Slicing (µm) | 0.3 | |
| Laser power (%) | 35 | |
| Scan speed (µm/s) | 10000 |
25x IP-PDMS
Si is a preferred substrate. Other substrates must have a refractive index of 1.6 or larger. Glass substrates must have ITO or another film with high refractive index deposited on the printing surface.
Observe sample dimensions before loading. For the standard sample holder the sample must be 25 mm × 25 mm and more than 0.5 mm thick, but not thicker than 0.7 mm. Contact the tool trainer before loading different samples.
| Application | Parameter | Value |
|---|---|---|
Standard | Hatching (µm) | 0.3 |
| Slicing (µm) | 0.3 | |
| Laser power (%) | 80 | |
| Scan speed (µm/s) | 30000 |